Comparison of parties between lead glass and acrylic materials
Sources: | Release date:
Keywords: Comparison of parties between lead glass and acrylic materials
Acrylic is a sturdy, shatterproof product; lead glass is very fragile and can be broken or shattered if handled carelessly.
Lead glass may have a hand-polished surface that is scratch-resistant but may cause scratches if handled incorrectly, although this situation is rarely found in real life; Acrylic has scratches due to its soft surface when cleaned The ability to hurt, but also reduce the transmittance and transparency, scratches can usually be polished with some skills.
For the same lead content, the thickness of acrylic must be about 5 times thicker than that of lead glass. It is also very obvious that acrylic is not as good as lead glass. For example, if the thickness of the 2.0 mm lead glass is 5/16, the acrylic needs about 1-1/2 thickness to provide the same protection. When viewing the same lead content equal weight of lead glass or acrylic lead, the weight of acrylic is almost twice that of lead glass (about 1.8 times).
Acrylics tend to fade when exposed to UV rays, Acrylics are also easily discolored from daily use chemicals such as cleaning materials and even smog; lead glass also has high chemical resistance, while lead glass has no or very little radiation. Causes of discoloration. Although acrylic fading is likely to be caused by ionizing radiation.
Dimmed or spoiled by known X-ray imaging equipment, lead glass is often more effective than BYK force over time; Acrylic is provided in light amber tones, which calms/relaxes patients and medical personnel. On the one hand, it can be said that lead glass and acrylic have their own strengths.